Double component, reaction drying topcoat paint. It is successfully used in corrosive environments due to its high adhesion ability and high resistance to external factors. It is recommended to be applied after Zinc Phosphate Primer and base coat applications for metal, after U-pox Lacquer application for Concrete Surfaces.
AREAS OF USE
Industrial plants,
Steel Constructions In Constructions Such As Ports, Bridges, Dams,
Chemical plants, pipelines, acid, alkali and solvent tanks,
Swimming pools and other pools.
APPLICATION
Surface Preparation:
Concrete surfaces should be thoroughly cleaned, dust and loose particles should be removed with a rotating steel or vacuum cleaner.
The scraped surface should be cleaned with dry air.
Sand blasting at SA 2.5 is recommended for surface cleaning.
Product Preparation and Application:
The mixing ratio should be 20 kg of Component A and 6 kg of Component B by weight.
Component A should be mixed with a low speed mixer until homogenized.
Component B should then be added to component A and the mixture should be mixed at about 100 rpm for at least 2 minutes.
As the amount of contents you are mixing increases, you may need to increase your mixing time or mixing speed.
As soon as you start mixing, there will be a cloudy appearance in the system at first, and as the mixing continues, it will start to become transparent again.
After opening the package, ISOWEIR U-POX TOP COAT is homogenized by thoroughly mixing, preferably with a drill motor, and mixed with the second component at the specified ratio.
The environment should be very well ventilated during indoor applications, and tools and processes related to electricity and flame should not be in the same environment due to the solvents contained in the primer.
Points to be Considered:
Eyes should be protected during the application.
It is recommended to wear gloves.
FEATURES, ADVANTAGES:
It provides long-term resistance in gasoline, jet fuel, ammonia water, NaOH, KOH, NaCl, sulfur dioxide, sea water, animal oils and sugary solutions.